Project PISA Phosphorus Influence on Steel Ageing

The integrity of the pressure vessel is vital to the safe operation of a nuclear reactor. It is therefore necessary to monitor or predict the changes in the reactor pressure vessel (RPV) material during operation. Exposure to irradiation (or elevated temperatures) causes the segregation of phosphorus to internal grain boundaries in RPV steels. This, in turn, encourages brittle intergranular failure of the material. The PISA project had the objective of reducing the uncertainties associated with the impact of this failure mechanism on the properties of the RPV, both during service and at the end-of-life. This report presents the experimental results on the segregation of P and C during irradiation and thermal treatments, and the associated mechanical property changes, generated within PISA. The new data cover a range of bulk P levels, irradiation temperatures and fluences, steel types and product forms.